Hi,
In addition to the other enumerated standards, you have to take into consideration EN 1011-3: Welding
Recommendations for welding of metallic materials. Part 3: Arc welding of stainless steels
Regards
Chavdarov
Цитат от pankaj.johri@in.transport.bombardier.com:
> Hi,
>
> Can anybody suggest what tests must be conducted to check welding quality
> of Duplex SS.
> Is there any European standard for these tests details.
>
> BR,
>
> Pankaj Johri, GradIEAust,
>
> _______________________________________________________________________________________________________________
>
> This e-mail communication (and any attachment/s) may contain confidential
> or privileged information and is intended only for the individual(s) or
> entity named above and to others who have been specifically authorized to
> receive it. If you are not the intended recipient, please do not read,
> copy, use or disclose the contents of this communication to others. Please
> notify the sender that you have received this e-mail in error by reply
> e-mail, and delete the e-mail subsequently. Please note that in order to
> protect the security of our information systems an AntiSPAM solution is in
> use and will browse through incoming emails.
> Thank you.
> _________________________________________________________________________________________________________________
>
>
> Ce message (ainsi que le(s) fichier(s)), transmis par courriel, peut
> contenir des renseignements confidentiels ou proteges et est destine a
> l?usage exclusif du destinataire ci-dessus. Toute autre personne est, par
> les presentes, avisee qu?il est strictement interdit de le diffuser, le
> distribuer ou le reproduire. Si vous l?avez recu par inadvertance,
> veuillez nous en aviser et detruire ce message. Veuillez prendre note
> qu'une solution antipollupostage (AntiSPAM) est utilisee afin d'assurer la
> securite de nos systemes d'information et qu'elle furetera les courriels
> entrants.
> Merci.
> _________________________________________________________________________________________________________________
>
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding-unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel
> views and meant for educational purposes only, Users must take their
> own decisions w.r.t. applicable code/standard/contract documents.
>
-------------------------------------
Ето тази оферта за хостинг чаках...
37 555 MB дисково пространство, 3 755 GB трафик на месец, 500 пощ. кутии, 8
независими сайта на един акаунт - САМО за 9,75 лв./месец!
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
Subscribe to:
Post Comments (Atom)
Blog Archive
-
▼
2010
(5182)
-
▼
March
(255)
- [MW:4398] Additive of Al
- [MW:4399] RE: 4393] RE: Failure of PQR in All Weld...
- Re: [MW:4400] proposed wps
- Re: [MW:4401] DSS REPAIR WELDING PROCEDURE
- Re: [MW:4402] Failure of PQR in All Weld Tensile
- Re: [MW:4406] Additive of Al
- RE: [MW:4404] RE: 4393] RE: Failure of PQR in All ...
- [MW:4403] Heat treatment of materials/flanges
- [MW:4405] Re: Heat treatment of materials/flanges
- [MW:4407] evaluating based on AWS D1.1 for UT
- [MW:4408] evaluation for PHASED ARRAY
- [MW:4409] Re: Failure of PQR in All Weld Tensile
- RE: [MW:4411] evaluation for PHASED ARRAY
- Re: [MW:4410] evaluating based on AWS D1.1 for UT
- [MW:4412] WPS
- Re: [MW:4413] evaluating based on AWS D1.1 for UT
- [MW:4414] RE: 4412] WPS
- Re: [MW:4415] WPS
- RE: [MW:4416] WPS
- [MW:4417] grain size of L450QC steel
- Re: [MW:4418] evaluation for PHASED ARRAY
- Re: [MW:4419] WPS
- [MW:4420] evaluation of phased array
- [MW:4421] Hispeed fluxes for SAW WELDING
- [MW:4422] Distance between welds
- RE: [MW:4423] Hispeed fluxes for SAW WELDING
- [MW:4424] RE: 4422] Distance between welds
- [MW:4425] Procedure qualification Record (PQR)
- [MW:4426] RE: 4425] Procedure qualification Record...
- Re: [MW:4427] Procedure qualification Record (PQR)...
- [MW:4428] colour of welding
- Re: [MW:4432] colour of welding
- Re: [MW:4431] Distance between welds
- [MW:4430] Material Properties :
- [MW:4429] ultrasonic testing method LIMITATIONS
- Re: [MW:4434] Distance between welds
- [MW:4433] RE: 4430] Material Properties :
- [MW:4435] RE: 4421] Hispeed fluxes for SAW WELDING...
- Re: [MW:4436] ultrasonic testing method LIMITATION...
- Re: [MW:4437] RE: 4421] Hispeed fluxes for SAW WEL...
- [MW:4438] Microstructure Segregation in Stainless ...
- Re: [MW:4439] RE: 4421] Hispeed fluxes for SAW WEL...
- Re: [MW:4440] Procedure qualification Record (PQR)...
- Re: [MW:4441] RE: 4425] Procedure qualification Re...
- Re: [MW:4442] ultrasonic testing method LIMITATION...
- Re: [MW:4443] Distance between welds
- Re: [MW:4444] Distance between welds
- RE: [MW:4445] Hispeed fluxes for SAW WELDING
- [MW:4446] colour of welding after SAW welding in l...
- Re: [MW:4447] colour of welding
- Re: [MW:4448] Procedure qualification Record (PQR)...
- [MW:4449] delta T test for material type II
- Re: Re: [MW:4451] Procedure qualification Record (...
- [MW:4450] WPS
- Re: [MW:4452] Procedure qualification Record (PQR)...
- Re: [MW:4453] Procedure qualification Record (PQR)...
- Re: [MW:4455] Procedure qualification Record (PQR)...
- Re: [MW:4454] WPS
- Re: [MW:4456] Procedure qualification Record (PQR)...
- [MW:4457] hard-facing of duplex steels
- RE: [MW:4459] hard-facing of duplex steels
- Re: [MW:4460] Procedure qualification Record (PQR)...
- Re: [MW:4461] colour of welding
- [MW:4462] ASME IX
- [MW:4463] Pipe to Flange welding for PQR
- Re: [MW:4464] Additive of Al
- [MW:4465] Duplex Stainless Steel Pump casing
- [MW:4458] Re: Material Properties :
- Re: [MW:4466] Pipe to Flange welding for PQR
- Re: [MW:4467] Pipe to Flange welding for PQR
- Re: [MW:4468] Pipe to Flange welding for PQR
- Re: [MW:4469] colour of welding
- [MW:4470] Re: Duplex Stainless Steel Pump casing
- [MW:4481] Buttering as per ASME VIII
- Re: [MW:4482] Duplex Stainless Steel Pump casing
- Re: [MW:4483] ASME IX
- Re: [MW:4471] Re: Duplex Stainless Steel Pump casi...
- [MW:4472] Why maximum PWHT temp shall be at least ...
- Re: [MW:4473] Why maximum PWHT temp shall be at le...
- [MW:4475] Test Specimen Heat Treatment
- [MW:4476] Low OCV of welding machine
- [MW:4474] Pipe length required for Welder Qualific...
- RE: [MW:4484] Why maximum PWHT temp shall be at le...
- Re: [MW:4477] Pipe length required for Welder Qual...
- Re: [MW:4478] Pipe length required for Welder Qual...
- Re: [MW:4479] Low OCV of welding machine
- Re: [MW:4480] Pipe to Flange welding for PQR
- [MW:4485] Copper to steel welding
- Re: Re: [MW:4486] colour of welding
- Re: [MW:4487] Copper to steel welding
- Re: [MW:4488] Buttering as per ASME VIII
- Re: [MW:4489] Copper to steel welding
- Re: [MW:4490] Copper to steel welding
- [MW:4494] Welding of Brasses & Bronzes
- [MW:4493] Re: Duplex Stainless Steel Pump casing
- Re: [MW:4492] Duplex Stainless Steel Pump casing
- Re: [MW:4491] Pipe to Flange welding for PQR
- [MW:4495] Welder Qualification as per ASME IX
- [MW:4496] RE: 4495] Welder Qualification as per AS...
- Re: Re: [MW:4498] Copper to steel welding
- Re: [MW:4497] Welding of Brasses & Bronzes
- [MW:4499] depth of root concavity
- RE: [MW:4500] Why maximum PWHT temp shall be at le...
- Re: [MW:4501] depth of root concavity
- [MW:4502] ASTM A216 Vs ASME SA216 Difference
- Re: [MW:4503] depth of root concavity
- [MW:4504] Welding consumables (2.25Cr-1Mo-0.25V) w...
- [MW:4505] Re: ASME IX
- [MW:4506] Re: depth of root concavity
- Re: [MW:4507] ASTM A216 Vs ASME SA216 Difference
- Re: [MW:4508] Welder Qualification as per ASME IX
- [MW:4509] RE: 4502] ASTM A216 Vs ASME SA216 Differ...
- Re: RE: [MW:4510] Why maximum PWHT temp shall be a...
- RE: [MW:4511] hard-facing of duplex steels
- Re: [MW:4512] RE: 4502] ASTM A216 Vs ASME SA216 Di...
- Re: [MW:4513] RE: 4502] ASTM A216 Vs ASME SA216 Di...
- [MW:4514] Hardness value of A543 Type-B, Class-1
- Re: [MW:4515] ASTM A216 Vs ASME SA216 Difference
- RE: [MW:4516] hard-facing of duplex steels
- [MW:4517] tests for checking welding quality of Du...
- [MW:4519] Pipeline NDT crawler using magnetic sign...
- [MW:4518] Re: tests for checking welding quality o...
- [MW:4520] RE: 4518] Re: tests for checking welding...
- [MW:4521] RE: 4520] RE: 4518] Re: tests for checki...
- RE: [MW:4522] hard-facing of duplex steels
- Re: [MW:4523] tests for checking welding quality o...
- Re: [MW:4524] Pipeline NDT crawler using magnetic ...
- Re: [MW:4525] RE: 4520] RE: 4518] Re: tests for ch...
- [MW:4526] Repair on casting
- [MW:4528] RE: 4526] Repair on casting
- [MW:4527] Information regarding safety valve in ho...
- Re: [MW:4529] RE: 4520] RE: 4518] Re: tests for ch...
- [MW:4530] evaluation of detrimental effect of stra...
- [MW:4531] qualified range for base metal
- Re: [MW:4532] Hardness value of A543 Type-B, Class...
- [MW:4533] RE: 4531] qualified range for base metal...
- Re: [MW:4534] Hardness value of A543 Type-B, Class...
- RE: [MW:4535] Hardness value of A543 Type-B, Class...
- Re: [MW:4536] Why maximum PWHT temp shall be at le...
- Re: [MW:4537] RE: 4531] qualified range for base m...
- Re: [MW:4538] Information regarding safety valve i...
- Re: [MW:4539] evaluation of detrimental effect of ...
- RE: [MW:4540] RE: 4531] qualified range for base m...
- [MW:4541] Re: Hispeed fluxes for SAW WELDING
- [MW:4542] Re: Welding of Brasses & Bronzes
- [MW:4543] Tracer Joints
- [MW:4544] Welding of steel to plastic
- [MW:4545] relevance of ferrite number test for dup...
- Re: [MW:4546] Tracer Joints
- Re: [MW:4547] Welding of steel to plastic
- Re: [MW:4548] Welding of steel to plastic
- [MW:4549] WeldDilution calculation
- [MW:4550] Chemical composition check of clad weld
- Re: [MW:4551] Tracer Joints
- [MW:4552] HDPE Joints
- RE: [MW:4553] relevance of ferrite number test for...
- Re: [MW:4554] Tracer Joints
- Re: [MW:4555] Chemical composition check of clad w...
- Re: [MW:4556] Tracer Joints
- Re: [MW:4557] Test Specimen Heat Treatment
- Re: [MW:4558] colour of welding after SAW welding ...
- [MW:4559] Repair on casting
- Re: Re: [MW:4560] Tracer Joints
- Re: Re: [MW:4561] Tracer Joints
- Re: [MW:4562] WeldDilution calculation
- RE: [MW:4563] Repair on casting
- Re: [MW:4564] Repair on casting
- [MW:4565] Re: Re: Welding of Brasses & Bronzes...
- Fw: Re: Re: [MW:4566] Test Specimen Heat Treatment...
- Re: Fw: Re: Re: [MW:4567] Test Specimen Heat Treat...
- [MW:4568] Fiber elongation of dish heads
- [MW:4569] problem with progression
- Re: [MW:4570] Fiber elongation of dish heads
- RE: [MW:4571] Fiber elongation of dish heads
- Re: [MW:4572] problem with progression
- Re: [MW:4573] Fiber elongation of dish heads
- [MW:4574] Re: Repair on casting
- Re: Re: [MW:4575] problem with progression
- [MW:4576] PIPE SUPPORTS AS PER ASME B 31.1
- [MW:4577] EN10204 3.2 certification
- [MW:4578] Alloy 20 in DI Water service
- Re: [MW:4581] EN10204 3.2 certification
- RE: [MW:4580] Alloy 20 in DI Water service
- [MW:4579] Certification Course on Coating Inspecti...
- [MW:4582] corrosion problem in TP321 pipes after h...
- [MW:4583] RE: 4582] corrosion problem in TP321 pip...
- [MW:4584] RE: 4582] corrosion problem in TP321 pip...
- [MW:4585] Re: EN10204 3.2 certification
- [MW:4586] Piping welding Electrode Consumption
- Re: [MW:4587] Piping welding Electrode Consumption...
- RE: [MW:4588] Piping welding Electrode Consumption...
- [MW:4589] RE: Welding of Brasses & Bronzes
- Re: [MW:4590] Piping welding Electrode Consumption...
- [MW:4591] Experience in using A193 B8 Cl.2 boltin...
- Re: [MW:4592] RE: 4582] corrosion problem in TP321...
- FW: [MW:4593] Alloy 20 in DI Water service
- RE: [MW:4594] RE: 4582] corrosion problem in TP321...
- Re: [MW:4595] RE: 4582] corrosion problem in TP321...
- Re: [MW:4596] Piping welding Electrode Consumption...
- Re: [MW:4597] Experience in using A193 B8 Cl.2 bo...
- Re: [MW:4598] RE: 4582] corrosion problem in TP321...
- [MW:4599] Hydrotest Duration for HDPE U/G Piping
- Re: [MW:4600] HDPE Joints
- [MW:4601] Duplex & Superduplex
- RE: [MW:4602] Duplex & Superduplex
- [MW:4603] Code limit of porosity and penetration a...
- FW: [MW:4604] Duplex & Superduplex
- [MW:4605] Welding consumable for SS 329
- [MW:4606] RE: 4605] Welding consumable for SS 329
- [MW:4607] RE: 4606] RE: 4605] Welding consumable f...
- [MW:4608] RE: 4606] RE: 4605] Welding consumable f...
- RE: [MW:4609] RE: 4606] RE: 4605] Welding consumab...
- [MW:4610] exposure time calculation for CS & SS
- Re: [MW:4612] exposure time calculation for CS & S...
- Re: [MW:4611] exposure time calculation for CS & S...
- Re: [MW:4613] exposure time calculation for CS & S...
- RE: [MW:4614] exposure time calculation for CS & S...
- Re: [MW:4615] exposure time calculation for CS & S...
- Re: [MW:4616] exposure time calculation for CS & S...
- [MW:4617] uniform distrubution of austenite in fer...
- [MW:4623] Weld A182 F91 TO SS 316
- [MW:4618] An Awareness programme on NDE @ Chennai ...
- [MW:4619] Need help regarding cutting blade materi...
- RE: [MW:4588] Duplex & Superduplex
- [MW:4620] Material Grd B53 And SA106-B
- Re: [MW:4621] Material Grd B53 And SA106-B
- [MW:4624] RE: 4623] Weld A182 F91 TO SS 316
- [MW:4629] welding electrode calculation
- Re: [MW:4625] Weld A182 F91 TO SS 316
- [MW:4627] MW: -4617 uniform distribution of austen...
- RE: [MW:4626] Material Grd B53 And SA106-B
- Re: [MW:4628] Material Grd B53 And SA106-B
- [MW:4630] Bolts failure
- Re: [MW:4631] Bolts failure
- Re: [MW:4632] Bolts failure
- Re: [MW:4633] Bolts failure
- [MW:4634] Re: MW: -4617 uniform distribution of au...
- Re: [MW:4635] Re: MW: -4617 uniform distribution o...
- Re: [MW:4636] Bolts failure
- [MW:4637] SA965/SA788
- [MW:4638] RE: 4637] SA965/SA788
- [MW:4639] RE: 4637] SA965/SA788
- [MW:4640] Back gouging of SS
- Re: [MW:4641] Back gouging of SS
- [MW:4642] NACE Test Requirements
- [MW:4644] Sub contract of weders(UW 26) (d)
- Re: [MW:4643] Back gouging of SS
- Re: [MW:4645] NACE Test Requirements
- Re: [MW:4647] Sub contract of weders(UW 26) (d)
- Re: [MW:4646] Back gouging of SS
- [MW:4648] Multiple PQRs for Impact test requiremen...
- Re: [MW:4649] Sub contract of weders(UW 26) (d)
- Re: [MW:4650] Bolts failure
- Re: [MW:4651] Multiple PQRs for Impact test requir...
- Re: [MW:4655] Sub contract of weders(UW 26) (d)
-
▼
March
(255)
No comments:
Post a Comment